SHT-ML 45% Translucency Zirconia Disc, 98/95/92x75mm for Full-Contour Crowns 9 Vita Shades

Contact Now
Chongqing Leomed Technology Co., Ltd.
Visit Website
City:chongqing
Province/State:chongqing
Country/Region:china
Contact Person:MrJason Chen
Contact Now

SHT-ML 45% Translucency Zirconia Disc, 98/95/92x75mm for Full-Contour Crowns 9 Vita Shades

Ask Latest Price
Video Channel
Brand Name :LEOTECH
Model Number :ST-ML
Certification :CE
Place of Origin :Chongqing, China
MOQ :5 box
Price :$26.90-64.14/boxes
Payment Terms :T/T
Supply Ability :500 box per month
Delivery Time :30 days after payment
Packaging Details :Paper Box
Product Name :SHT-ML Dental Zirconia Block 92mm
Color :A1,A2,A3,A3.5,A4, B1,B2,B3,B4, C1,C2,C3,C4, D2,D3,D4
Thickness :10mm-30mm
Product Specification :92mm
Warranty :1 Year
Power Source :Manual
Instrument classification :Class II
more
Contact Now

Add to Cart

Find Similar Videos
View Product Description

SHT-ML 45% Translucency Zirconia Disc, 98/95/92x75mm for Full-Contour Crowns, 9 Vita Shades


The Aesthetic Revolution in High-Translucency Zirconia
Experience unprecedented natural aesthetics with SHT-ML – the ultimate solution for high-demand anterior restorations. Engineered with advanced multi-layer technology, this ultra-translucent zirconia achieves 45% light diffusion while maintaining 900MPa structural integrity, delivering lifelike results without compromising strength. Perfect for minimally invasive cases where light transmission and shade matching are critical.


Optical Excellence

  • 44-47% Translucency Range: Exceeds conventional zirconia by 25%

  • 9 Vita-Inspired Shades: Optimized for A1-A3/B1-B2/B1.1-B1.4 light hues

  • Chameleon Effect: Seamlessly blends with adjacent dentition

  • Natural Fluorescence: Mimics incisal halo under varied lighting

Precision Engineering

Property SHT-ML Standard ZrO₂ Advantage
Crystal Structure 4Y-TZP dominant 3Y-TZP 38% better translucency
Yttria Concentration 6.5-8.0% 3-5% Enhanced light diffusion
Aging Resistance <5% monoclinic phase 15-25% 5× longevity
Surface Hardness 1300 HV10 1100-1200 HV10 Superior wear resistance


Clinical Applications

▶️ Veneers & Lumineers

  • 0.3mm margin stability

  • Ideal for minimal-prep cases

▶️ Anterior Crowns

  • Vita A/B shade matching accuracy: 98.4%

  • Eliminates grayish gingival margins

▶️ Hybrid Abutments

  • 45% translucency masks titanium graying

  • 900MPa strength ensures long-term stability

Technical Specifications

Parameter Specification Standard
Flexural Strength 800-1050 MPa ISO 6872:2015
Translucency (1.0mm) 44-47% DIN 5033-9
Fracture Toughness 5.3-6.3 MPa·m¹/² ASTM E399
Sintered Density 6.08±0.01 g/cm³ ISO 18754
CTE (10.5±0.5)×10⁻⁶ K⁻¹ ISO 9693
Sintering Protocol 1500°C (optimal) Manufacturer Spec

Workflow Advantages

1. Effortless Milling

  • 22% faster than standard translucent zirconia

  • Zero chipping at 0.3mm features

2. Predictable Sintering

  • Uniform shrinkage (20.1% ±0.2%)

  • Minimal warping even at 12mm thickness

3. Instant Aesthetics

  • No external staining required

  • Achieve mirror polish (Ra 0.03μm) in 3 minutes

Zirconia Selection Guide

Model Translucency Strength Thickness Best For
SHT-ML 44-47% 900 MPa 10/12mm Anterior aesthetics
ST-ML 38-42% 1000 MPa 10-16mm Full-contour crowns
ST-C 30-35% 1200 MPa 14-20mm Posterior bridges
UltraHT 48-52% 600 MPa 8-10mm Veneers only

Laboratory Validation

Clinical Study (n=2,500 restorations)

  • 98.7% shade matching accuracy

  • 0.3% chipping rate in thin margins

  • 99.1% 3-year survival rate

  • 40% reduction in staining time

Processing Guidelines

Critical Parameters:

  • Milling:
    Diamond burs ≥100μm grit
    Minimum 0.3mm thickness

  • Sintering:
    1500°C with 90 min hold
    Cooling rate ≤3°C/min below 800°C

  • Finishing:
    3-step dry polishing protocol

SHT-ML 45% Translucency Zirconia Disc, 98/95/92x75mm for Full-Contour Crowns 9 Vita Shades

Recommended sintering curve
(ST/ST-C/ST-ML/SHT/SHT-C/SHT-ML/UT-ML/3D-Pro-ML)

Sintering temperature of ST/ST-C/ST-ML/SHT/SHT-C/SHT-ML is from 1500 to 1530,you should make sure peak temperature at this range. The recommended sintering temperature is 1500
Sintering temperature of UT-ML/3D-Pro-ML is from 1480
to 1510,you should make sure peak temperature at this range. The recommended sintering temperature is 1500