Full-Zirconia Restoration Block, Fracture Toughness 5.3-6.3MPa·m¹/², 800-1050MPa Flexural Strength
The Smart Choice for Digital Dental Labs
Streamline your production with SHT-ML – the high-translucency zirconia engineered for modern CAD/CAM workflows. Combining 45% light transmission with 900MPa strength, this material delivers consistent results across milling systems while reducing processing time by 35%. With 9 optimized shades and warp-free sintering, achieve first-pass success on 98% of anterior cases.
CAD/CAM Ecosystem Compatibility
| Parameter | Specification |
|---|---|
| Milling Speed | 45,000 RPM optimal |
| Tool Life | 180 discs/bur |
| Sintering Shrinkage | 20.1% ±0.2% |
| Marginal Accuracy | <20μm gap |
| Surface Finish | Ra 0.03μm post-polish |
Problem-Solution Matrix
| Lab Challenge | SHT-ML Solution |
|---|---|
| Inconsistent shrinkage | ±0.2% predictable shrinkage |
| Veneer chipping | 0.3mm edge stability |
| Shade mismatches | 9 Vita-optimized hues |
| Warped frameworks | Warp-free sintering |
| Slow milling | 25% faster machining |
| Metric | Improvement | Annual Savings* |
|---|---|---|
| Material Waste | 68% less | $14,500 |
| Remake Costs | 89% less | $32,000 |
| Milling Time | 25% faster | $18,000 |
| Staining Labor | 100% eliminated | $9,200 |
| *Based on medium lab processing 400 discs/year |
24/7 Technical Hotline
Milling parameter optimization
Sintering profile troubleshooting
Case failure analysis
Digital Assets
3Shape Device Library
exocad Material Presets
Roland DG Tool Paths
Education Portal
On-demand video tutorials
Monthly live Q&A sessions
Case study library
A: Yes - recommended coolant temp <25°C
Q: Minimum margin width?
A: 0.3mm with chamfer design
Q: Sintering support for small furnaces?
A: Optimal for 120-150mm chamber sizes
Q: Shade stability after glazing?
A: Delta E<0.5 color shift
Recommended sintering curve
(ST/ST-C/ST-ML/SHT/SHT-C/SHT-ML/UT-ML/3D-Pro-ML)
| Sintering temperature of ST/ST-C/ST-ML/SHT/SHT-C/SHT-ML is from 1500℃ to 1530℃,you should make sure peak temperature at this range. The recommended sintering temperature is 1500℃ Sintering temperature of UT-ML/3D-Pro-ML is from 1480℃ to 1510℃,you should make sure peak temperature at this range. The recommended sintering temperature is 1500℃ | ||