Fast-Sinter SHT Zirconia Block , 90-Minute Turnaround , 1500°C Protocol
Transform same-day dentistry with SHT's optimized sintering protocol – full density in 90 minutes at 1500°C. The material's low thermal mass enables 8°C/minute heating rates without cracking, while the white base allows real-time shade adjustments during try-in.
Chairside Workflow
Time Savings vs. Competitors
| Process | SHT | Industry Avg |
| Staining | 7 min | 15 min |
| Sintering | 90 min | 120 min |
| Total Chairtime | 115 min | 165 min |
Product paramenters | Model | SHT-White |
| Size | 98mm,95mm,92*75mm |
| Translucency | 46% |
| Sizes | 10mm/12mm/14mm/16mm/18mm/20mm/22mm/25mm |
| Strength | 1000 MPa |
ST/SHT/SHT-ML Sintering
Max Heating rate: 10℃ per minute
Final temperature: 1500℃-1550℃, 1530℃ is best
Holding time at final temperature: 2 hours
Cooling should be done without temperature control in closed furnace
Never open the furnace before it has reached a temperature of less than 80℃ to avoid thermal shocks
Sintering charts: